Continuous Fiber Reinforced Thermoplastics
Haziran 19, 2022
Sürekli elyaf takviyeli termoplastiklerin yüksek hızlı şekillendirilmesi hakkında bilgi almak için aşağıdaki linke tıklayınız.
Forming processes of continuous fiber reinforced thermoplastic materials are oftentimes limited to high volume production due to the high costs for tooling and processing machines.
This study suggests the combined use of a cold and simple tool and high forming speeds to reduce tooling and processing costs and enable the usage of common stamping machines.
Half sphere samples are produced from single and two-layer poly-propylene and glass fiber organo-sheets in a custom built drop tower and analyzed for their geometry, degree of re-consolidation, surface quality and potential fiber damage using a variety of microscopy techniques.
While only mediocre degrees of re-consolidation and limited surface qualities can be achieved with the combination of a cold tooling and state-of-the-art forming speeds of 0–0.5 ms−1, the usage of a higher forming speed of 3 ms−1 , vastly improves surface qualities and the degree of re-consolidation without any detectable fiber damage.
This effect is more pronounced in the dual layer material. Extensive knowledge on the forming behavior of continuous fiber reinforced thermoplastics at high cooling rates and high speeds of deformation is required for sufficient process control and future studies need to further elaborate and quantify the influencing factors and limits of high-speed forming of continuous fiber reinforced thermoplastics.